Titanium Grade 1
UNS R50250
Resumen
Commercially pure titanium with the highest ductility and formability of all titanium grades. Lowest strength but best corrosion resistance in oxidizing environments. The preferred grade for chemical processing equipment, plate-type heat exchangers, and applications requiring extensive cold forming. Excellent weldability with no post-weld heat treatment required.
Composición Química (% en peso)
| Elemento | Mín | Máx |
|---|---|---|
| Ti (Titanio) | 99.2 | — |
| C (Carbono) | — | 0.08 |
| Fe (Hierro) | — | 0.2 |
| O (Oxígeno) | — | 0.18 |
| N (Nitrógeno) | — | 0.03 |
| H (Hidrógeno) | — | 0.015 |
Propiedades Mecánicas
| Propiedad | Valor | Condición |
|---|---|---|
| Resistencia a la Tracción | ≥ 240 MPa (35 ksi) | — |
| Límite Elástico (0.2%) | ≥ 170 MPa (25 ksi) | — |
| Elongación | ≥ 24% | — |
| Dureza | ≤ 70 HRB | recocido |
| Densidad | 4.51 g/cm³ | — |
Propiedades Físicas
| Propiedad | Valor |
|---|---|
| Punto de Fusión | 1668 °C |
| Conductividad Térmica | 16.4 W/m·K (at 20°C) |
| Resistividad Eléctrica | 0.56 µΩ·m |
Resistencia a la Corrosión
Outstanding resistance to seawater and chloride environments at all temperatures up to 315°C. Completely immune to chloride stress corrosion cracking. Excellent resistance to oxidizing acids including nitric acid and chromic acid. Resistant to wet chlorine gas. Not recommended for reducing acids (HCl, H₂SO₄) or hydrofluoric acid.
Aplicaciones Típicas